Investigation of the 3D Printability of Covalently Cross-Linked Polypeptide-Based Hydrogels
Johnel Giliomee, Lisa C. du Toit, Bert Klumperman, and Yahya E. Choonara*
PUBLISHED IN: ACS Publications
ABSTRACT
The 3D printability of poly(l-lysine-ran–l-alanine) and four-arm poly(ethylene glycol) (P(KA)/4-PEG) hydrogels as 3D biomaterial inks was investigated using two approaches to develop P(KA)/4-PEG into 3D biomaterial inks. Only the “composite microgel” inks were 3D printable. In this approach, P(KA)/4-PEG hydrogels were processed into microparticles and incorporated into a polymer solution to produce a composite microgel paste. Polymer solutions composed of either 4-arm PEG-acrylate (4-PEG-Ac), chitosan (CS), or poly(vinyl alcohol) (PVA) were used as the matrix material for the composite paste. The three respective composite microgel inks displayed good 3D printability in terms of extrudability, layer-stacking ability, solidification mechanism, and 3D print fidelity. The biocompatibility of P(KA)/4-PEG hydrogels was retained in the 3D printed scaffolds, and the biofunctionality of bioinert 4-PEG and PVA hydrogels was enhanced. CS-P(KA)/4-PEG inks demonstrated excellent 3D printability and proved highly successful in printing scaffolds with a narrow strand diameter (∼200 μm) and narrow strand spacing (∼500 μm) while the integrity of the vertical and horizontal pores was maintained. Using different needle IDs and strand spacing, certain physical properties of the hydrogels could be tuned, while the 3D printed porosity was kept constant. This included the surface area to volume ratio, the macropore sizes, and the mechanical properties. The scaffolds demonstrated adequate adhesion and spreading of NIH 3T3 fibroblasts seeded on the scaffold surfaces for 4 days. Consequently, the scaffolds were considered suitable for potential applications in wound healing, as well as other soft tissue engineering applications. Apart from the contribution to new 3D biomaterial inks, this work also presented a new and facile method of processing covalently cross-linked hydrogels into 3D printed scaffolds. This could potentially “unlock” the 3D printability of biofunctional hydrogels, which are generally excluded from 3D printing applications.
Related Scientific Publications
Design Characteristics of a Neoteric, Superhydrophilic, Mechanically Robust Hydrogel Engineered […]
Dermal fibroblasts play a pivotal role in cell therapy, serving as versatile cells essential for tissue repair and regeneration. Their unique ability to produce extracellular matrix components contributes significantly to the efficacy and success of various cell-based therapies in treating skin-related conditions and wounds. Scaling up the production of dermal fibroblasts poses a challenge due to their limited lifespan in culture and the need to maintain their specialized functions over multiple generations...
3D bioprinting has emerged as a viable tool to fabricate 3D tissue constructs with high precision using various bioinks which offer instantaneous gelation, shape fidelity, and cytocompatibility. Among various bioinks, cellulose is the most abundantly available natural polymer & widely used as bioink for 3D bioprinting applications. To mitigate the demanding crosslinking needs of cellulose, it is frequently chemically modified or blended with other polymers to develop stable hydrogels. In this study, we have developed a thermoresponsive...
Hyaluronic acid (HA) is a glycosaminoglycan in the extracellular matrix with immunoregulatory properties depending on its molecular weight (MW). However, the impact of matrix-bound HA on dendritic cells (DCs) remains unclear due to varying distribution of HA MW under different physiological conditions. To investigate DCs in defined biosystems, 3D collagen matrices modified with HA of specific MW with similar microstructure and HA levels are used. It is found that HA MW influences...
The aim of this study was to assess how transglutaminase (TG) impacts the microstructure, texture, and rheological properties of fermentation-induced pea protein emulsion gels. Additionally, the study examined the influence of storage time on the functional properties of these gels. Fermentation-induced pea protein gels were produced in the presence or absence of TG and stored for 1, 4, 8, 12, and 16 weeks. Texture analysis, rheological measurements, moisture content and microstructure evaluation...
Current treatments for glioblastoma (GBM) face challenges due to rapidly occurring tumor recurrences. In response, researchers have developed localized drug delivery systems, notably AT101-GlioMesh - an alginate-based mesh embedded with AT101-loaded PLGA microspheres. Fabricated for high encapsulation efficiency, this system ensures a sustained release of AT101, demonstrating a significant cytotoxic effect on GBM cell lines. This promising development could potentially revolutionize GBM therapy and prevent tumor recurrence.